Revealing the relation between microstructural heterogeneities and local mechanical properties of complex-phase steel by correlative electron microscopy and nanoindentation characterization
Materials & Design, vol. 203, pp. 109620
Abstract
Compositional and microstructural heterogeneity are characteristics of modern multiphase steels. However, the quantitative characterization of these heterogeneities is rarely considered in scientific publications. We characterized the compositional and microstructural heterogeneity of a commercial complex-phase steel (CP800) by combining various electron microscopy techniques and nanoindentation. Compositional gradients of C and Mn were characterized qualitatively and quantitatively through electron probe microanalysis (EPMA). Electron backscatter diffraction (EBSD) results were utilized to identify and segment the microstructural constituents. A novel nanoindentation approach was used to obtain hardness maps. Cube-corner indenter and micro-newton load were applied to limit the indent depth and spacing between adjacent indents to the nanometer scale. A high-resolution hardness map was obtained and successfully overlapped with EPMA and EBSD results, based on which the correlation between compositional heterogeneity and hardness variation in complex-phase microstructure was successfully established.
Authors 6
-
Affiliation as printed
Steel Institute, RWTH Aachen University, Aachen 52072, Germany
-
Affiliation as printed
Steel Institute, RWTH Aachen University, Aachen 52072, Germany
-
Affiliation as printed
Bruker Nano Surfaces, Aachen 52068, Germany
-
Affiliation as printed
Central Facility for Electron Microscopy, RWTH Aachen University, Aachen 52074, Germany
-
Affiliation as printed
Steel Institute, RWTH Aachen University, Aachen 52072, Germany
-
Affiliation as printed
Steel Institute, RWTH Aachen University, Aachen 52072, Germany
Cited by 61 stored of 62
No patents citing this paper on Lens.org (checked 2026-10-06).